ALCROME – SBF

Recubrimiento con excepcional adhesión en sustratos de MD y HSS. Especially recommended for cutting tools, due to its high thermal resistance.
Specifically focused process for drilling processes, improves the surface finish of the coating vs ALCROME – F.

Coating properties

Structure

Monolayer

Process temperature [ºC].

450 Coefficient of friction

0.20 Components

Al, Cr, N

Maximum working temperature [ºC].

1000

Nanohardness [HV]

4200

Thickness [µm] Thickness [µm

3.5 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3 Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – SBF

Coating properties

Structure

Monolayer

Process temperature [ºC].

450

Coefficient of friction

0.20

Components

Al, Cr, N

Maximum working temperature [ºC].

1000

Nanohardness [HV]

4200

Thickness [µm] Thickness [µm

3.5 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

Monolayer

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

Applications

See our list of coatings

Contact us

Spain

France

Spain

France

PVD coatings

Projects Completed

Metal Estalki