ALTINE

Coating with an exceptionally high aluminium content, which makes it harder than conventional TiAlN coatings. Good adhesion on MD and HSS substrates. Especially recommended for cutting tools, both drilling and milling.

Coating properties

Structure

Monolayer

Process temperature [ºC].

450 °C

Coefficient of friction

0.6 Components

Al, Ti, N

Maximum working temperature [ºC].

800 °C

Nanohardness [HV]

3800 HV

Thickness [µm] Thickness [µm

2.5 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25 Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE

Coating properties

Structure

Monolayer

Process temperature [ºC].

450 °C

Coefficient of friction

0.6

Components

Al, Ti, N

Maximum working temperature [ºC].

800 °C

Nanohardness [HV]

3800 HV

Thickness [µm] Thickness [µm

2.5 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

Applications

See our list of coatings

Contact us

Spain

France

Spain

France

PVD coatings

Projects Completed

Metal Estalki