CRN

Nitruro de Cromo

General purpose coating for cutting, forming, injection moulding and tribological applications. High oxidation resistance, very good substrate adhesion and very good adhesion strength.

Coating properties

Structure

Monolayer

Process temperature [ºC].

450 Coefficient of friction

0.3 Components

Cr, N

Maximum working temperature [ºC].

800 Roughness

0.14 Nanohardness [HV]

1800

Thickness [µm] Thickness [µm

3 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2 Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

CRN-F

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

CRN

Nitruro de Cromo

Coating properties

Structure

Monolayer

Process temperature [ºC].

450

Coefficient of friction

0.3

Components

Cr, N

Maximum working temperature [ºC].

800

Roughness

0.14

Nanohardness [HV]

1800

Thickness [µm] Thickness [µm

3 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

Monolayer

Cr, N

1800 HV

450 °C

800 °C

3 µm±0.5

0.2