Revêtements PVD / Outils de coupe

Perçage

Foret ALTIN - SBF vs ALTIN - F, ce processus de finition améliore les propriétés tribologiques de vos outils

Revêtements pour le perçage

01. Acier

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.55

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

TIN – F

Monocapa

Ti, N

2400 HV

450 °C

600 °C

2.5 µm±0.5

0.45

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

02. Fonte

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

03. Fritté

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – F

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.3

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

TRINACO RED – SBF

Multinanogradiente

Al, Ti, Si, N

4500 HV

450 °C

1200 °C

2.5 µm±0.5

0.25

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALTINE – SBF

Monocapa

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.25

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.6

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – F

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.3

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

ALCROME – SBF

Monocapa

Al, Cr, N

4200 HV

450 °C

1000 °C

3.5 µm±0.5

0.20

04. Titane/Inconel

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

05. Inoxydable

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

06. Métaux composites

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

07. Aluminio

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

08. Aciers durs

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Titre

Structure

Composants

Nanodura

T° processus

T° max. fct.

Épaisseur

Coef. friction

Voir le fichier

Voir notre liste de revêtements