ALTINE – SBF

Coating with an extraordinarily high aluminium content, which makes it harder than conventional TiAlN coatings. Good adhesion on MD and HSS substrates. Especially recommended for cutting tools, both drilling and milling.
Specifically focused process for drilling processes, improves the surface finish of the coating vs. ALTINE – F.

Coating properties

Structure

Monolayer

Process temperature [ºC].

450 Coefficient of friction

0.25 Components

Al, Ti, N

Maximum working temperature [ºC].

800 Nanohardness [HV]

3800

Thickness [µm] Thickness [µm

2.5 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3 Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – F

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

ALTINE – SBF

Coating properties

Structure

Monolayer

Process temperature [ºC].

450

Coefficient of friction

0.25

Components

Al, Ti, N

Maximum working temperature [ºC].

800

Nanohardness [HV]

3800

Thickness [µm] Thickness [µm

2.5 µm±0.5

Coating variants

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

Designation

Structure

Components

Nanohardness

Process temperature

Max. working temperature

Thickness

Coef. friction

See file

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.6

Monolayer

Al, Ti, N

3800 HV

450 °C

800 °C

2.5 µm±0.5

0.3

Applications

See our list of coatings

Contact us

Spain

France

Spain

France

PVD coatings

Projects Completed

Metal Estalki